Designated as UNS N02200 & W.Nr. 2.4060 & 2.4066, Nickel 200 is solid solution strengthened and commercially pure wrought nickel. It has good mechanical properties and excellent resistance to many corrosive environments. Nickel 200 is primarily used in food processing industry due to its corrosion resistance. It can also be used in applications involving reducing chemicals, caustic alkalies, distilled and natural waters, alkaline salt solutions, dry fluorine, and synthetic fibers. Depending on the specific product form, Nickel 200 may be furnished with different heat treatment and delivery conditions which result in different mechanical properties (tensile strength, yield strength, elongation, reduction of area, hardness, etc).

1. Chemical Composition Requirements

Chemical Composition of Nickel 200, %
Nickel(plus Cobalt)	≥99.0
Copper	≤0.25
Iron	≤0.40
Manganese	≤0.35
Carbon	≤0.15
Silicon	≤0.35
Sulfur	≤0.01

2. Physical Properties

Physical Properties of Nickel 200
Density		Melting Range		Specific Heat		Curie Temperature
lb/in3	g/cm3	°F	°C	Btu/lb*°F	J/kg*°C	°F	°C
0.321	8.89	2615-2635	1435-1446	0.109	456	680	360

3. Product Forms & Standards

Nickel 200: Product Forms and Relative Standards
Products form	Standard
Rod and bar	ASTM B160, DIN 17752, ISO9723
Pipe and Tube	ASTM B161, B163, B725, B730, B751, B775, B829, DIN 17751, ISO 6207
Plate, Sheet & Strip	ASTM B162, DIN 17750, ISO 6208
Fittings	ASTM B366
Forgings	ASTM B564, ISO 9725, DIN17754
Wire	DIN 17753, ISO 9724